Riddle solved: Why was Roman concrete so durable?

An unexpected ancient manufacturing strategy may hold the key to designing concrete that lasts for millennia.
Press Inquiries

Press Contact:

Abby Abazorius
Phone: 617-253-2709
MIT News Office

Media Download

On left, Roman concrete structures of Privernum, Italy with icy puddles, orange sky, and rural location. On right, the concrete fragment is colorized with rainbow colors, including a prominent section colored red.
Download Image
Caption: A large-area elemental map (Calcium: red, Silicon: blue, Aluminum: green) of a 2 cm fragment of ancient Roman concrete (right) collected from the archaeological site of Privernum, Italy (left). A calcium-rich lime clast (in red), which is responsible for the unique self-healing properties in this ancient material, is clearly visible in the lower region of the image.
Credits: Courtesy of the researchers
The concrete fragment is colorized with rainbow colors, including a prominent section colored red.
Download Image
Caption: A calcium-rich lime clast (in red), which is responsible for the unique self-healing properties in this ancient material, is clearly visible in the lower region of the large-area elemental map (Calcium: red, Silicon: blue, Aluminum: green) of a 2 cm fragment of ancient Roman concrete.
Credits: Courtesy of the researchers

*Terms of Use:

Images for download on the MIT News office website are made available to non-commercial entities, press and the general public under a Creative Commons Attribution Non-Commercial No Derivatives license. You may not alter the images provided, other than to crop them to size. A credit line must be used when reproducing images; if one is not provided below, credit the images to "MIT."

Close
On left, Roman concrete structures of Privernum, Italy with icy puddles, orange sky, and rural location. On right, the concrete fragment is colorized with rainbow colors, including a prominent section colored red.
Caption:
A large-area elemental map (Calcium: red, Silicon: blue, Aluminum: green) of a 2 cm fragment of ancient Roman concrete (right) collected from the archaeological site of Privernum, Italy (left). A calcium-rich lime clast (in red), which is responsible for the unique self-healing properties in this ancient material, is clearly visible in the lower region of the image.
Credits:
Courtesy of the researchers

The ancient Romans were masters of engineering, constructing vast networks of roads, aqueducts, ports, and massive buildings, whose remains have survived for two millennia. Many of these structures were built with concrete: Rome’s famed Pantheon, which has the world’s largest unreinforced concrete dome and was dedicated in 128 C.E., is still intact, and some ancient Roman aqueducts still deliver water to Rome today. Meanwhile, many modern concrete structures have crumbled after a few decades.

Researchers have spent decades trying to figure out the secret of this ultradurable ancient construction material, particularly in structures that endured especially harsh conditions, such as docks, sewers, and seawalls, or those constructed in seismically active locations.

Now, a team of investigators from MIT, Harvard University, and laboratories in Italy and Switzerland, has made progress in this field, discovering ancient concrete-manufacturing strategies that incorporated several key self-healing functionalities. The findings are published today in the journal Science Advances, in a paper by MIT professor of civil and environmental engineering Admir Masic, former doctoral student Linda Seymour ’14, PhD ’21, and four others.

For many years, researchers have assumed that the key to the ancient concrete’s durability was based on one ingredient: pozzolanic material such as volcanic ash from the area of Pozzuoli, on the Bay of Naples. This specific kind of ash was even shipped all across the vast Roman empire to be used in construction, and was described as a key ingredient for concrete in accounts by architects and historians at the time.

Under closer examination, these ancient samples also contain small, distinctive, millimeter-scale bright white mineral features, which have been long recognized as a ubiquitous component of Roman concretes. These white chunks, often referred to as “lime clasts,” originate from lime, another key component of the ancient concrete mix. “Ever since I first began working with ancient Roman concrete, I’ve always been fascinated by these features,” says Masic. “These are not found in modern concrete formulations, so why are they present in these ancient materials?”

Previously disregarded as merely evidence of sloppy mixing practices, or poor-quality raw materials, the new study suggests that these tiny lime clasts gave the concrete a previously unrecognized self-healing capability. “The idea that the presence of these lime clasts was simply attributed to low quality control always bothered me,” says Masic. “If the Romans put so much effort into making an outstanding construction material, following all of the detailed recipes that had been optimized over the course of many centuries, why would they put so little effort into ensuring the production of a well-mixed final product? There has to be more to this story.”

Upon further characterization of these lime clasts, using high-resolution multiscale imaging and chemical mapping techniques pioneered in Masic’s research lab, the researchers gained new insights into the potential functionality of these lime clasts.

Historically, it had been assumed that when lime was incorporated into Roman concrete, it was first combined with water to form a highly reactive paste-like material, in a process known as slaking. But this process alone could not account for the presence of the lime clasts. Masic wondered: “Was it possible that the Romans might have actually directly used lime in its more reactive form, known as quicklime?”

Studying samples of this ancient concrete, he and his team determined that the white inclusions were, indeed, made out of various forms of calcium carbonate. And spectroscopic examination provided clues that these had been formed at extreme temperatures, as would be expected from the exothermic reaction produced by using quicklime instead of, or in addition to, the slaked lime in the mixture. Hot mixing, the team has now concluded, was actually the key to the super-durable nature.

“The benefits of hot mixing are twofold,” Masic says. “First, when the overall concrete is heated to high temperatures, it allows chemistries that are not possible if you only used slaked lime, producing high-temperature-associated compounds that would not otherwise form. Second, this increased temperature significantly reduces curing and setting times since all the reactions are accelerated, allowing for much faster construction.”

During the hot mixing process, the lime clasts develop a characteristically brittle nanoparticulate architecture, creating an easily fractured and reactive calcium source, which, as the team proposed, could provide a critical self-healing functionality. As soon as tiny cracks start to form within the concrete, they can preferentially travel through the high-surface-area lime clasts. This material can then react with water, creating a calcium-saturated solution, which can recrystallize as calcium carbonate and quickly fill the crack, or react with pozzolanic materials to further strengthen the composite material. These reactions take place spontaneously and therefore automatically heal the cracks before they spread. Previous support for this hypothesis was found through the examination of other Roman concrete samples that exhibited calcite-filled cracks.

To prove that this was indeed the mechanism responsible for the durability of the Roman concrete, the team produced samples of hot-mixed concrete that incorporated both ancient and modern formulations, deliberately cracked them, and then ran water through the cracks. Sure enough: Within two weeks the cracks had completely healed and the water could no longer flow. An identical chunk of concrete made without quicklime never healed, and the water just kept flowing through the sample. As a result of these successful tests, the team is working to commercialize this modified cement material.

“It’s exciting to think about how these more durable concrete formulations could expand not only the service life of these materials, but also how it could improve the durability of 3D-printed concrete formulations,” says Masic.

Through the extended functional lifespan and the development of lighter-weight concrete forms, he hopes that these efforts could help reduce the environmental impact of cement production, which currently accounts for about 8 percent of global greenhouse gas emissions. Along with other new formulations, such as concrete that can actually absorb carbon dioxide from the air, another current research focus of the Masic lab, these improvements could help to reduce concrete’s global climate impact.

The research team included Janille Maragh at MIT, Paolo Sabatini at DMAT in Italy, Michel Di Tommaso at the Instituto Meccanica dei Materiali in Switzerland, and James Weaver at the Wyss Institute for Biologically Inspired Engineering at Harvard University. The work was carried out with the assistance of the Archeological Museum of Priverno in Italy.

Press Mentions

New York Times

Prof. Admir Masic speaks with New York Times reporter Amos Zeeberg about his research studying the benefits of lime clasts – a material used in ancient Roman infrastructure. According to Masic’s research, “these lime clasts were actually reservoirs of calcium that helped fill in cracks, making the concrete self-healing,” writes Zeeberg. “As cracks formed, water would seep in and dissolve the calcium in the lime, which then formed solid calcium carbonate, essentially creating new rock that filled in the crack.”

Associated Press

In an article about how researchers are exploring why ancient Roman and Mayan buildings are still standing, AP reporter Maddie Burakoff highlights how researchers from MIT found that an ancient Roman technique for manufacturing concrete gave the material “self-healing” properties. “We don’t need to make things last quite as long as the Romans did to have an impact,” says Prof. Admir Masic. If we add 50 or 100 years to concrete’s lifespan, “we will require less demolition, less maintenance and less material in the long run.”

Wired

Researchers at MIT have discovered what makes ancient Roman concrete “exponentially more durable than modern concrete,” reports Jim Morrison for Wired. “Creating a modern equivalent that lasts longer than existing materials could reduce climate emissions and become a key component of resilient infrastructure,” writes Morrison.

Scientific American

MIT researchers have discovered that ancient Romans used calcium-rich mineral deposits to build durable infrastructure, reports Daniel Cusick for Scientific American. This “discovery could have implications for reducing carbon emissions and creating modern climate-resilient infrastructure,” writes Cusick.

NPR

Prof. Admir Masic speaks with NPR host Scott Simon about the concrete blend used by the ancient Romans to build long standing infrastructures. “We found that there are key ingredients in ancient Roman concrete that lead to a really outstanding functionality property in the ancient mortar, which is self-healing,” explains Masic.

Reuters

Reuters reporter Will Dunham writes that a new study by MIT researchers uncovers the secret ingredient that made ancient Roman concrete so durable and could “pave the way for the modern use of a replicated version of this ancient marvel.” Prof. Admir Masic explains that the findings are “an important next step in improving the sustainability of modern concretes through a Roman-inspired strategy.”

The Guardian

Researchers at MIT and elsewhere have found that using ancient Roman techniques for creating concrete could be used to create buildings with longer lifespans, reports Nicola Davis for The Guardian. “Roman-inspired approaches, based for example on hot mixing, might be a cost-effective way to make our infrastructure last longer through the self-healing mechanisms we illustrate in this study,” says Prof. Admir Masic.

CNN

MIT researchers have discovered that ancient Romans used lime clasts when manufacturing concrete, giving the material self-healing properties, reports Katie Hunt for CNN. "Concrete allowed the Romans to have an architectural revolution," explains Prof. Admir Masic. "Romans were able to create and turn the cities into something that is extraordinary and beautiful to live in. And that revolution basically changed completely the way humans live."

Fast Company

Fast Company reporter Adele Peters writes that researchers from MIT and other institutions have found that a technique employed by ancient Romans for manufacturing concrete contains self-healing properties and could be used to help reduce concrete’s global carbon footprint. The ancient concrete method could open the “opportunity to build infrastructure that is self-healing infrastructure,” explains Prof. Admir Masic.

The Hill

Researchers at MIT have found that applying ancient Roman techniques for developing concrete could be used to reduce concrete manufacturing emissions, reports Saul Elbein for The Hill. “Researchers said blocks treated with the method — in which concrete was mixed with reactive quicklime under continuous heat — knit themselves back together within a few weeks after being fractured,” writes Elbein.

Science

Scientists from MIT and other institutions have uncovered an ingredient called quicklime used in ancient Roman techniques for manufacturing concrete that may have given the material self-healing properties, reports Jacklin Kwan for Science Magazine. When the researchers made their own Roman concrete and tested to see how it handled cracks, “the lime lumps dissolved and recrystallized, effectively filling in the cracks and keeping the concrete strong,” Kwan explains.