Tiny pores in graphene could give rise to membranes

New membranes may filter water or separate biological samples.
Press Inquiries

Press Contact:

Caroline McCall
Phone: 617-253-2700
MIT News Office

Media Download

The researchers' membrane, consisting of graphene on a polycarbonate track etch membrane (the graphene is the darker region in the center of the white film). The total membrane is about 2 cm wide by 1 cm tall, while the graphene portion is about 5 mm by 5 mm.
Download Image
Caption: The researchers' membrane, consisting of graphene on a polycarbonate track etch membrane (the graphene is the darker region in the center of the white film). The total membrane is about 2 cm wide by 1 cm tall, while the graphene portion is about 5 mm by 5 mm.
A scanning electron microscope image of the graphene covering pores in the polycarbonate track etch membrane.
Download Image
Caption: A scanning electron microscope image of the graphene covering pores in the polycarbonate track etch membrane.
A high-resolution scanning transmission electron microscope image taken at Oak Ridge National Laboratory showing a large hole in the graphene (black region in the center). The image is 32 nm by 32 nm, hence the hole is about 10 nm in diameter. The white on the surface of the graphene is contamination, which is a recurring problem for anyone imaging graphene using this technique.
Download Image
Caption: A high-resolution scanning transmission electron microscope image taken at Oak Ridge National Laboratory showing a large hole in the graphene (black region in the center). The image is 32 nm by 32 nm, hence the hole is about 10 nm in diameter. The white on the surface of the graphene is contamination, which is a recurring problem for anyone imaging graphene using this technique.
Credits: Image courtesy of Juan-Carlos Idrobo
Another high-resolution scanning transmission electron microscope image taken at Oak Ridge National Laboratory showing a small hole in the graphene (small black region slightly below the center). The image is 8 nm by 8 nm, meaning that the hole is 0.5 nm in diameter. In this image the honeycomb structure of graphene lattice is clearly seen.
Download Image
Caption: Another high-resolution scanning transmission electron microscope image taken at Oak Ridge National Laboratory showing a small hole in the graphene (small black region slightly below the center). The image is 8 nm by 8 nm, meaning that the hole is 0.5 nm in diameter. In this image the honeycomb structure of graphene lattice is clearly seen.
Credits: Image courtesy of Juan-Carlos Idrobo

*Terms of Use:

Images for download on the MIT News office website are made available to non-commercial entities, press and the general public under a Creative Commons Attribution Non-Commercial No Derivatives license. You may not alter the images provided, other than to crop them to size. A credit line must be used when reproducing images; if one is not provided below, credit the images to "MIT."

Close
The researchers' membrane, consisting of graphene on a polycarbonate track etch membrane (the graphene is the darker region in the center of the white film). The total membrane is about 2 cm wide by 1 cm tall, while the graphene portion is about 5 mm by 5 mm.
Caption:
The researchers' membrane, consisting of graphene on a polycarbonate track etch membrane (the graphene is the darker region in the center of the white film). The total membrane is about 2 cm wide by 1 cm tall, while the graphene portion is about 5 mm by 5 mm.
A scanning electron microscope image of the graphene covering pores in the polycarbonate track etch membrane.
Caption:
A scanning electron microscope image of the graphene covering pores in the polycarbonate track etch membrane.
A high-resolution scanning transmission electron microscope image taken at Oak Ridge National Laboratory showing a large hole in the graphene (black region in the center). The image is 32 nm by 32 nm, hence the hole is about 10 nm in diameter. The white on the surface of the graphene is contamination, which is a recurring problem for anyone imaging graphene using this technique.
Caption:
A high-resolution scanning transmission electron microscope image taken at Oak Ridge National Laboratory showing a large hole in the graphene (black region in the center). The image is 32 nm by 32 nm, hence the hole is about 10 nm in diameter. The white on the surface of the graphene is contamination, which is a recurring problem for anyone imaging graphene using this technique.
Credits:
Image courtesy of Juan-Carlos Idrobo
Another high-resolution scanning transmission electron microscope image taken at Oak Ridge National Laboratory showing a small hole in the graphene (small black region slightly below the center). The image is 8 nm by 8 nm, meaning that the hole is 0.5 nm in diameter. In this image the honeycomb structure of graphene lattice is clearly seen.
Caption:
Another high-resolution scanning transmission electron microscope image taken at Oak Ridge National Laboratory showing a small hole in the graphene (small black region slightly below the center). The image is 8 nm by 8 nm, meaning that the hole is 0.5 nm in diameter. In this image the honeycomb structure of graphene lattice is clearly seen.
Credits:
Image courtesy of Juan-Carlos Idrobo

Much has been made of graphene’s exceptional qualities, from its ability to conduct heat and electricity better than any other material to its unparalleled strength: Worked into a composite material, graphene can repel bullets better than Kevlar. Previous research has also shown that pristine graphene — a microscopic sheet of carbon atoms arranged in a honeycomb pattern — is among the most impermeable materials ever discovered, making the substance ideal as a barrier film.

But the material may not be as impenetrable as scientists have thought. By engineering relatively large membranes from single sheets of graphene grown by chemical vapor deposition, researchers from MIT, Oak Ridge National Laboratory (ORNL) and elsewhere have found that the material bears intrinsic defects, or holes in its atom-sized armor. In experiments, the researchers found that small molecules like salts passed easily through a graphene membrane’s tiny pores, while larger molecules were unable to penetrate.

The results, the researchers say, point not to a flaw in graphene, but to the possibility of promising applications, such as membranes that filter microscopic contaminants from water, or that separate specific types of molecules from biological samples.

“No one has looked for holes in graphene before,” says Rohit Karnik, associate professor of mechanical engineering at MIT. “There’s a lot of chemical methods that can be used to modify these pores, so it’s a platform technology for a new class of membranes.”

Karnik and his colleagues, including researchers from the Indian Institute of Technology and King Fahd University of Petroleum and Minerals, have published their results in the journal ACS Nano.

Karnik worked with MIT graduate student Sean O’Hern to look for materials “that could lead to not just incremental changes, but substantial leaps in terms of the way membranes perform.” In particular, the team cast around for materials with two key attributes, high flux and tunability: that is, membranes that quickly filter fluids, but are also easily tailored to let certain molecules through while trapping others. The group settled on graphene, in part because of its extremely thin structure and its strength: A sheet of graphene is as thin as a single atom, but strong enough to let high volumes of fluids through without shredding apart.

The team set out to engineer a membrane spanning 25 square millimeters — a surface area that is large by graphene standards, holding about a quadrillion carbon atoms. They used graphene synthesized by chemical vapor deposition, borrowing on expertise from the research group of Jing Kong, the ITT Career Development Associate Professor of Electrical Engineering at MIT. The team then developed techniques to transfer the graphene sheet to a polycarbonate substrate dotted with holes.

Once the researchers successfully transferred the graphene, they began to experiment with the resulting membrane, exposing it to flowing water containing molecules of varying sizes. They theorized that if graphene were indeed impermeable, the molecules would be blocked from flowing across. However, experiments showed otherwise, as researchers observed salts flowing through the membrane.

As another test, the team exposed a copper foil with graphene grown on it to a chemical agent that dissolves copper. Instead of protecting the metal, graphene let the agent through, corroding the underlying copper. To test the size of the pores within graphene, the group attempted to filter water with larger molecules. It appeared that there was a limit to the size of the pores, as larger molecules were unable to pass through the membrane.

As a final experiment, Karnik and O’Hern observed the actual holes in the graphene membrane, looking at the material through a high-powered electron microscope at ORNL in collaboration with Juan-Carlos Idrobo. They found that pores ranged in size from about 1 to 12 nanometers — just wide enough to selectively let some small molecules through.

“Right now we know from this characterization how the graphene behaves, and what kind of intrinsic pores it has,” Karnik says. “In some sense it’s the first step to practically realizing graphene-based membranes.”

Karnik adds that a near-term application for such membranes may include a portable sensor in which a layer of graphene “could shield the sensor from the environment,” letting through only a molecule or contaminant of interest. Another use may be in drug delivery, with graphene, dotted with pores of a determined size, delivering therapies in a controlled release.

“We’re right now in the process of transferring more graphene to different substrates and making holes of our own, making a viable membrane for water filtration,” O’Hern says.

Scott Bunch, an assistant professor of mechanical engineering at the University of Colorado, says the group’s results are the first demonstration that graphene bears defects. The membrane developed by the group “has the potential to be a revolutionary membrane” that separates particles at the molecular scale.

“The issue that now needs to be addressed is whether one can discriminate between smaller molecules,” Bunch says. “Once this happens, graphene membranes will eventually live up to the truly remarkable properties that they promise.”

Other researchers involved in the work are Cameron Stewart, Michael Boutilier, Sreekar Bhaviripudi, Sarit Das, Tahar Laoui and Muataz Atieh. This work was funded by the King Fahd University of Petroleum and Minerals through the Center for Clean Water and Clean Energy at MIT and KFUPM, and was also supported by the ORNL ShaRE program.