Researchers clarify mystery about proposed battery material

Study explains conflicting results from other experiments, may lead to batteries with more energy per pound.
Press Inquiries

Press Contact:

Karl-Lydie Jean-Baptiste
Phone: (617) 253-1682
MIT News

Media Download

This series of photographs shows the chemical reaction that occurs during the charging of a lithium oxygen battery using lithium iodide as an additive.
Download Image
Caption: This series of photographs shows the chemical reaction that occurs during the charging of a lithium oxygen battery using lithium iodide as an additive.
Credits: Photo: Jose-Luis Olivares/MIT
Iodide ions can make water more reactive, altering the reaction pathway during the discharge process.
Download Image
Caption: Iodide ions can make water more reactive, altering the reaction pathway during the discharge process.
Credits: Courtesy of the researchers
Lithium oxygen battery cell components were used for experiments in the lab.
Download Image
Caption: Lithium oxygen battery cell components were used for experiments in the lab.
Credits: Photo: Karl-Lydie Jean-Baptiste/MIT

*Terms of Use:

Images for download on the MIT News office website are made available to non-commercial entities, press and the general public under a Creative Commons Attribution Non-Commercial No Derivatives license. You may not alter the images provided, other than to crop them to size. A credit line must be used when reproducing images; if one is not provided below, credit the images to "MIT."

Close
This series of photographs shows the chemical reaction that occurs during the charging of a lithium oxygen battery using lithium iodide as an additive.
Caption:
This series of photographs shows the chemical reaction that occurs during the charging of a lithium oxygen battery using lithium iodide as an additive.
Credits:
Photo: Jose-Luis Olivares/MIT
Iodide ions can make water more reactive, altering the reaction pathway during the discharge process.
Caption:
Iodide ions can make water more reactive, altering the reaction pathway during the discharge process.
Credits:
Courtesy of the researchers
Lithium oxygen battery cell components were used for experiments in the lab.
Caption:
Lithium oxygen battery cell components were used for experiments in the lab.
Credits:
Photo: Karl-Lydie Jean-Baptiste/MIT

Battery researchers agree that one of the most promising possibilities for future battery technology is the lithium-air (or lithium-oxygen) battery, which could provide three times as much power for a given weight as today’s leading technology, lithium-ion batteries. But tests of various approaches to creating such batteries have produced conflicting and confusing results, as well as controversies over how to explain them.

Now, a team at MIT has carried out detailed tests that seem to resolve the questions surrounding one promising material for such batteries: a compound called lithium iodide (LiI). The compound was seen as a possible solution to some of the lithium-air battery’s problems, including an inability to sustain many charging-discharging cycles, but conflicting findings had raised questions about the material’s usefulness for this task. The new study explains these discrepancies, and although it suggests that the material might not be suitable after all, the work provides guidance for efforts to overcome LiI’s drawbacks or find alternative materials.

The new results appear in the journal Energy and Environmental Science, in a paper by Yang Shao-Horn, MIT’s W.M. Keck Professor of Energy; Paula Hammond, the David H. Koch Professor in Engineering and head of the Department of Chemical Engineering; Michal Tulodziecki, a recent MIT postdoc at the Research Laboratory of Electronics; Graham Leverick, an MIT graduate student; Yu Katayama, a visiting student; and three others.

The promise of the lithium-air battery comes from the fact one of the two electrodes, which are usually made of metal or metal oxides, is replaced with air that flows in and out of the battery; a weightless substance is thus substituted for one of the heavy components. The other electrode in such batteries would be pure metallic lithium, a lightweight element.

But that theoretical promise has been limited in practice because of three issues: the need for high voltages for charging, a low efficiency with regard to getting back the amount of energy put in, and low cycle lifetimes, which result from instability in the battery’s oxygen electrode. Researchers have proposed adding lithium iodide in the electrolyte as a way of addressing these problems. But published results have been contradictory, with some studies finding the LiI does improve the cycling life, “while others show that the presence of LiI leads to irreversible reactions and poor battery cycling,” Shao-Horn says.

Previously, “most of the research was focused on organics” to make lithium-air batteries feasible, says Michal Tulodziecki, the paper’s lead author. But most of these organic compounds are not stable, he says, “and that’s why there’s been a great focus on lithium iodide [an inorganic material], which some papers said helps the batteries achieve thousands of cycles. But others say no, it will damage the battery.” In this new study, he says, “we explored in detail how lithium iodide affects the process, with and without water,” a comparison which turned out to be significant.

The team looked at the role of LiI on lithium-air battery discharge, using a different approach from most other studies. One set of studies was conducted with the components outside of the battery, which allowed the researchers to zero in on one part of the reaction, while the other study was done in the battery, to help explain the overall process.

They then used ultraviolet and visible-light spectroscopy and other techniques to study the reactions that took place. Both of these processes foster the production of different lithium compound such as LiOH (lithium hydroxide) in the presence of both LiI and water, instead of Li2O2 (lithium peroxide).  LiI can enhance water’s reactivity and make it lose protons more easily, which promotes the formation of LiOH in these batteries and interferes with the charging process. These observations show that finding ways to suppress these reactions could make compounds such as LiI work better.

This study could point the way toward selecting a different compound instead of LiI to perform its intended function of suppressing unwanted chemical reactions at the electrode surface, Leverick says, adding that this work demonstrates the importance of “looking at the detailed mechanism carefully.”

Shao-Horn says that the new findings “help get to the bottom of this existing controversy on the role of LiI on discharge. We believe this clarifies and brings together all these different points of view.”

But this work is just one step in a long process of trying to make lithium-air technology practical, the researchers say. “There’s so much to understand,” says Leverick, “so there’s not one paper that’s going to solve it. But we will make consistent progress.”

“Lithium-oxygen batteries that run on oxygen and lithium ions are of great interest because they could enable electric vehicles of much greater range. However, one of the problems is that they are not very efficient yet," says Larry Curtiss, a distinguished fellow at Argonne National Laboratory, who was not involved in this work. In this study, he says, "it is shown how adding a simple salt, lithium iodide, can potentially be used to make these batteries run much more efficiently. They have provided new insight into how the lithium iodide acts to help break up the solid discharge product, which will help to enable the development of these advanced battery systems.”

Curtiss adds that “there are still significant barriers remaining to be overcome before these batteries become a reality, such as getting long enough cycle life, but this is an important contribution to the field.”

The team also included recent MIT graduates Chibueze Amanchukwu PhD ’17 and David Kwabi PhD ’16, and Fanny Bardé of Toyota Motor Europe. The work was supported by Toyota Motor Europe and the Skoltech Center for Electrochemical Energy Storage, and used facilities supported by the National Science Foundation.